Blend
61000IiQ
Manufacturer：LNP™ ELCRIN™
冲击改性，优异低温冲击，耐化学性，可着色
Recorded properties
Record date：2026-11-07
| Property | Value | Unit |
|---|---|---|
| Density | 1.19 | g/cm³ |
| Melt flow rate | 13.0 | g/10min |
| Tensile strength | 46.0 | MPa |
| Tensile modulus | 2050.0 | MPa |
| Elongation at break | 140.0 | % |
| Flexural modulus | 2000.0 | MPa |
| Notched impact strength | 55.0 | kJ/m² |
| HDT 1.8MPa | 99.0 | °C |
| HDT 0.45MPa | 75.0 | °C |
| Flame rating | HB class | — |
Test standard, specimen condition and source rights are not fully recorded. Values are for preliminary screening only; verify with the manufacturer before design or purchasing decisions.
Grade handling information to verify
The information below was automatically extracted from a material PDF and has not been individually reviewed. It is for preliminary reference only. Verify the exact grade’s manufacturer processing instructions, safety data sheet and equipment procedures before production; do not use candidate values directly as machine settings.
Matched by original PDF filename
- Storage
- Review the source for packaging, storage and opened-package instructions.
- Drying
- Candidate injection-molding recommendations: temperature 110 °C; time 4 - 6 h; processing moisture ≤0.02 %. Verify the source, grade and conditions.
- Equipment setup
- Candidate injection-molding recommendations: melt temperature 255 - 275 °C; mold temperature 40 - 90 °C. Verify the source, grade and conditions.
- Applications
- Candidate application areas in the source: automotive. Verify the source, exact use and applicable approvals.
Source: the matched material PDF; page numbers refer to the original PDF.
- Drying temperature：page 1
- Drying time：page 1
- Processing moisture：page 1
- Melt temperature：page 1
- Mold temperature：page 1
- Application areas：page 2