Polycarbonate (PC)
Compound DX13315C
Manufacturer：LNP™ STAT-KON™
LNP Clean Compounding Technology, 低LPC，低离子，低逸出，低C18-C40烃，导电
Recorded properties
Record date：2026-11-07
| Property | Value | Unit |
|---|---|---|
| Density | 1.26 | g/cm³ |
| Melt flow rate | 30.0 | g/10min |
| Tensile strength | 130.0 | MPa |
| Tensile modulus | 10600.0 | MPa |
| Elongation at break | 2.6 | % |
| Flexural strength | 199.0 | MPa |
| Flexural modulus | 9290.0 | MPa |
| Notched impact strength | 88.0 | kJ/m² |
| HDT 1.8MPa | 123.0 | °C |
Test standard, specimen condition and source rights are not fully recorded. Values are for preliminary screening only; verify with the manufacturer before design or purchasing decisions.
Grade handling information to verify
The information below was automatically extracted from a material PDF and has not been individually reviewed. It is for preliminary reference only. Verify the exact grade’s manufacturer processing instructions, safety data sheet and equipment procedures before production; do not use candidate values directly as machine settings.
Matched by original PDF filename
- Storage
- Review the source for packaging, storage and opened-package instructions.
- Drying
- Candidate injection-molding recommendations: temperature 90 - 110 °C; time 3 - 5 h. Verify the source, grade and conditions.
- Equipment setup
- Candidate injection-molding recommendations: melt temperature 280 - 320 °C; mold temperature 90 - 120 °C. Verify the source, grade and conditions.
- Applications
- Review the source and applicable approvals.
Source: the matched material PDF; page numbers refer to the original PDF.
- Drying temperature：page 1
- Drying time：page 1
- Melt temperature：page 1
- Mold temperature：page 1