Polycarbonate (PC) resin containing 10% glass fiber
THERMOCOMP™ Compound D151
Manufacturer：LNP™
高模量，良好表面，低翘曲，良好延展性，非溴化非氯化阻燃
Recorded properties
Record date：2026-11-07
| Property | Value | Unit |
|---|---|---|
| Density | 1.27 | g/cm³ |
| Melt flow rate | 27.5 | g/10min |
| Tensile strength | 82.0 | MPa |
| Tensile modulus | 4430.0 | MPa |
| Elongation at break | 3.6 | % |
| Flexural strength | 58.0 | MPa |
| Flexural modulus | 4010.0 | MPa |
| Notched impact strength | 13.0 | kJ/m² |
| HDT 1.8MPa | 121.0 | °C |
| HDT 0.45MPa | 117.0 | °C |
| Vicat softening point | 131.0 | °C |
| Flame rating | V-2 class | — |
Test standard, specimen condition and source rights are not fully recorded. Values are for preliminary screening only; verify with the manufacturer before design or purchasing decisions.
Grade handling information to verify
The information below was automatically extracted from a material PDF and has not been individually reviewed. It is for preliminary reference only. Verify the exact grade’s manufacturer processing instructions, safety data sheet and equipment procedures before production; do not use candidate values directly as machine settings.
Matched by original PDF filename
- Storage
- Review the source for packaging, storage and opened-package instructions.
- Drying
- Candidate injection-molding recommendations: temperature 110 °C; time 3 - 6 h; processing moisture ≤0.02 %. Verify the source, grade and conditions.
- Equipment setup
- Candidate injection-molding recommendations: melt temperature 285 - 310 °C; mold temperature 80 - 110 °C. Verify the source, grade and conditions.
- Applications
- Review the source and applicable approvals.
Source: the matched material PDF; page numbers refer to the original PDF.
- Drying temperature：page 2
- Drying time：page 2
- Processing moisture：page 2
- Melt temperature：page 2
- Mold temperature：page 2