Carbon Fiber Reinforced Polymer
LUPOY GN2101FB
Manufacturer：LG化学
阻燃，无卤
Recorded properties
Record date：2026-11-07
| Property | Value | Unit |
|---|---|---|
| Density | 1.25 | g/cm³ |
| Melt flow rate | 8.3 | g/10min |
| Tensile strength | 63.8 | MPa |
| Tensile modulus | 3620.0 | MPa |
| Elongation at break | 15.0 | % |
| Flexural strength | 105.0 | MPa |
| Flexural modulus | 3475.0 | MPa |
| Notched impact strength | 6.0 | kJ/m² |
| HDT 1.8MPa | 133.0 | °C |
| HDT 0.45MPa | 127.0 | °C |
| Vicat softening point | 136.0 | °C |
| Flame rating | V-0 | — |
Test standard, specimen condition and source rights are not fully recorded. Values are for preliminary screening only; verify with the manufacturer before design or purchasing decisions.
Grade handling information to verify
The information below was automatically extracted from a material PDF and has not been individually reviewed. It is for preliminary reference only. Verify the exact grade’s manufacturer processing instructions, safety data sheet and equipment procedures before production; do not use candidate values directly as machine settings.
Matched by original PDF filename
- Storage
- Review the source for packaging, storage and opened-package instructions.
- Drying
- Candidate injection-molding recommendations: temperature 100 - 120 °C; time 3 - 5 h; processing moisture ≤0.02 %. Verify the source, grade and conditions.
- Equipment setup
- Candidate injection-molding recommendations: melt temperature 300 - 340 °C; mold temperature 90 - 120 °C. Verify the source, grade and conditions.
- Applications
- Review the source and applicable approvals.
Source: the matched material PDF; page numbers refer to the original PDF.
- Drying temperature：page 2
- Drying time：page 2
- Processing moisture：page 2
- Melt temperature：page 2
- Mold temperature：page 2