PC-GF30
HFD4413
Manufacturer：LEXAN™
高流动性和优异的表面外观，内部模具释放
Recorded properties
Record date：2026-11-07
| Property | Value | Unit |
|---|---|---|
| Density | 1.43 | g/cm³ |
| Melt flow rate | 16.0 | g/10min |
| Tensile strength | 111.0 | MPa |
| Tensile modulus | 7870.0 | MPa |
| Elongation at break | 3.0 | % |
| Flexural modulus | 7760.0 | MPa |
| Notched impact strength | 12.0 | kJ/m² |
| HDT 1.8MPa | 130.0 | °C |
| Vicat softening point | 143.0 | °C |
| Flame rating | {'GWFI': '900°C', 'GWFI_class': 'HB', 'GWIT_1mm': '850°C', 'GWIT_2mm': '875°C', 'GWIT_3mm': '850°C'} | — |
Test standard, specimen condition and source rights are not fully recorded. Values are for preliminary screening only; verify with the manufacturer before design or purchasing decisions.
Grade handling information to verify
The information below was automatically extracted from a material PDF and has not been individually reviewed. It is for preliminary reference only. Verify the exact grade’s manufacturer processing instructions, safety data sheet and equipment procedures before production; do not use candidate values directly as machine settings.
Matched by original PDF filename
- Storage
- Review the source for packaging, storage and opened-package instructions.
- Drying
- Candidate injection-molding recommendations: temperature 120 °C; time 3 - 4 h; processing moisture ≤0.02 %. Verify the source, grade and conditions.
- Equipment setup
- Candidate injection-molding recommendations: melt temperature 290 - 310 °C; mold temperature 70 - 95 °C. Verify the source, grade and conditions.
- Applications
- Review the source and applicable approvals.
Source: the matched material PDF; page numbers refer to the original PDF.
- Drying temperature：page 2
- Drying time：page 2
- Processing moisture：page 2
- Melt temperature：page 2
- Mold temperature：page 2