Polycarbonate (PC)
THERMOCOMP™ Compound DX06313
Manufacturer：LNP
冲击改性，薄壁成型
Recorded properties
Record date：2026-11-07
| Property | Value | Unit |
|---|---|---|
| Density | 1.42 | g/cm³ |
| Melt flow rate | 42.0 | g/10min |
| Tensile strength | 99.0 | MPa |
| Tensile modulus | 7500.0 | MPa |
| Elongation at break | 3.6 | % |
| Flexural modulus | 7000.0 | MPa |
| Notched impact strength | 15.0 | kJ/m² |
| HDT 1.8MPa | 136.0 | °C |
| Vicat softening point | 142.0 | °C |
| Flame rating | Not specified | — |
Test standard, specimen condition and source rights are not fully recorded. Values are for preliminary screening only; verify with the manufacturer before design or purchasing decisions.
Grade handling information to verify
The information below was automatically extracted from a material PDF and has not been individually reviewed. It is for preliminary reference only. Verify the exact grade’s manufacturer processing instructions, safety data sheet and equipment procedures before production; do not use candidate values directly as machine settings.
Matched by original PDF filename
- Storage
- Review the source for packaging, storage and opened-package instructions.
- Drying
- Candidate injection-molding recommendations: temperature 120 °C; time 3 - 4 h; processing moisture ≤0.02 %. Verify the source, grade and conditions.
- Equipment setup
- Candidate injection-molding recommendations: melt temperature 315 - 340 °C; mold temperature 80 - 115 °C. Verify the source, grade and conditions.
- Applications
- Review the source and applicable approvals.
Source: the matched material PDF; page numbers refer to the original PDF.
- Drying temperature：page 1
- Drying time：page 1
- Processing moisture：page 1
- Melt temperature：page 1
- Mold temperature：page 1