PC-GF
INFINO HN-3204
Manufacturer：乐天化学公司
{'加工方式': '注塑成型', '交付形式': '颗粒，本色', '区域可用性': '北美，欧洲，亚太地区'}
Recorded properties
Record date：2026-11-07
| Property | Value | Unit |
|---|---|---|
| Density | 1.35 | g/cm³ |
| Melt flow rate | 9.0 | g/10min |
| Tensile strength | 88.0 | MPa |
| Tensile modulus | 5500.0 | MPa |
| Elongation at break | 4.0 | % |
| Flexural strength | 150.0 | MPa |
| Flexural modulus | 5400.0 | MPa |
| Notched impact strength | 7.0 | kJ/m² |
| HDT 1.8MPa | 143.0 | °C |
| HDT 0.45MPa | 138.0 | °C |
| Flame rating | {'UL_94_Flame_rating': 'V-0', 'Burning_behav_at_1.5_mm_nom_thickn_': 'V-0', 'Burning_behav_at_thickness_h': 'V-0', 'Burning_behav_5V_at_thickness_h': '5VA', 'Glow_Wire_Flammability_Index_GWFI': '960°C', 'Glow_Wire_Ignition_Temperature_GWIT': '825°C'} | — |
Test standard, specimen condition and source rights are not fully recorded. Values are for preliminary screening only; verify with the manufacturer before design or purchasing decisions.
Grade handling information to verify
The information below was automatically extracted from a material PDF and has not been individually reviewed. It is for preliminary reference only. Verify the exact grade’s manufacturer processing instructions, safety data sheet and equipment procedures before production; do not use candidate values directly as machine settings.
Matched by original PDF filename
- Storage
- Review the source for packaging, storage and opened-package instructions.
- Drying
- Candidate injection-molding recommendations: temperature 100 °C; time 4 h; processing moisture ≤0.05 %. Verify the source, grade and conditions.
- Equipment setup
- Candidate injection-molding recommendations: melt temperature 300 - 310 °C; mold temperature 80 - 100 °C. Verify the source, grade and conditions.
- Applications
- Review the source and applicable approvals.
Source: the matched material PDF; page numbers refer to the original PDF.
- Drying temperature：page 2
- Drying time：page 2
- Processing moisture：page 2
- Melt temperature：page 2
- Mold temperature：page 2