PC
Makrolon® 2407 RE
Manufacturer：科思创德国公司
通用型，低粘度，紫外线稳定，易脱模，部分生物闭环等级
Recorded properties
Record date：2026-11-07
| Property | Value | Unit |
|---|---|---|
| Density | 1.2 | g/cm³ |
| Melt flow rate | 20.0 | g/10min |
| Tensile strength | 66.0 | MPa |
| Tensile modulus | 2400.0 | MPa |
| Elongation at break | 50.0 | % |
| Flexural strength | 98.0 | MPa |
| Flexural modulus | 2350.0 | MPa |
| Notched impact strength | 65.0 | kJ/m² |
| Vicat softening point | 143.0 | °C |
| Flame rating | {'glow_wire_flammability_index': 850, 'glow_wire_ignition_temperature': 875, 'thickness_tested': '0.75 mm'} | — |
Test standard, specimen condition and source rights are not fully recorded. Values are for preliminary screening only; verify with the manufacturer before design or purchasing decisions.
Grade handling information to verify
The information below was automatically extracted from a material PDF and has not been individually reviewed. It is for preliminary reference only. Verify the exact grade’s manufacturer processing instructions, safety data sheet and equipment procedures before production; do not use candidate values directly as machine settings.
Matched by original PDF filename
- Storage
- Review the source for packaging, storage and opened-package instructions.
- Drying
- Candidate injection-molding recommendations: temperature 120 °C; time 2 - 3 h; processing moisture ≤0.02 %. Verify the source, grade and conditions.
- Equipment setup
- Candidate injection-molding recommendations: melt temperature 280 - 320 °C; mold temperature 80 - 120 °C. Verify the source, grade and conditions.
- Applications
- Review the source and applicable approvals.
Source: the matched material PDF; page numbers refer to the original PDF.
- Drying temperature：page 2
- Drying time：page 2
- Processing moisture：page 2
- Melt temperature：page 2
- Mold temperature：page 3