Polyetherimide (PEI)
STAT-KON™ Compound EX12310C
Manufacturer：LNP
LNP清洁复合技术，低C18-C40烃类，导电，尺寸稳定性
Recorded properties
Record date：2026-11-08
| Property | Value | Unit |
|---|---|---|
| Melt flow rate | 31.0 | g/10min |
| Tensile strength | 156.0 | MPa |
| Tensile modulus | 8970.0 | MPa |
| Elongation at break | 2.3 | % |
| Flexural modulus | 8410.0 | MPa |
| Notched impact strength | 3.0 | kJ/m² |
| HDT 1.8MPa | 201.0 | °C |
| Flame rating | V-0 class | — |
Test standard, specimen condition and source rights are not fully recorded. Values are for preliminary screening only; verify with the manufacturer before design or purchasing decisions.
Grade handling information to verify
The information below was automatically extracted from a material PDF and has not been individually reviewed. It is for preliminary reference only. Verify the exact grade’s manufacturer processing instructions, safety data sheet and equipment procedures before production; do not use candidate values directly as machine settings.
Matched by original PDF filename
- Storage
- Review the source for packaging, storage and opened-package instructions.
- Drying
- Candidate injection-molding recommendations: temperature 150 °C; time 4 - 6 h; processing moisture ≤0.02 %. Verify the source, grade and conditions.
- Equipment setup
- Candidate injection-molding recommendations: melt temperature 360 - 400 °C; mold temperature 140 - 180 °C. Verify the source, grade and conditions.
- Applications
- Review the source and applicable approvals.
Source: the matched material PDF; page numbers refer to the original PDF.
- Drying temperature：page 1
- Drying time：page 1
- Processing moisture：page 1
- Melt temperature：page 1
- Mold temperature：page 1