聚对苯二甲酸乙二醇酯
Rynite® SST35 NC010
Manufacturer：塞拉尼斯
超韧性，优良的力学性能，尺寸稳定性，抗蠕变，耐热性，优异的颜色稳定性，高表面光泽，固有的良好电气性能
Recorded properties
Record date：2026-11-08
| Property | Value | Unit |
|---|---|---|
| Density | 1.52 | g/cm³ |
| Melt flow rate | 1400.0 | g/10min |
| Tensile strength | 90.0 | MPa |
| Tensile modulus | 7500.0 | MPa |
| Elongation at break | 6.0 | % |
| Flexural strength | 145.0 | MPa |
| Flexural modulus | 6890.0 | MPa |
| Notched impact strength | 154.0 | kJ/m² |
| HDT 1.8MPa | 246.0 | °C |
| HDT 0.45MPa | 220.0 | °C |
| Flame rating | HB | — |
Test standard, specimen condition and source rights are not fully recorded. Values are for preliminary screening only; verify with the manufacturer before design or purchasing decisions.
Grade handling information to verify
The information below was automatically extracted from a material PDF and has not been individually reviewed. It is for preliminary reference only. Verify the exact grade’s manufacturer processing instructions, safety data sheet and equipment procedures before production; do not use candidate values directly as machine settings.
Matched by original PDF filename
- Storage
- Review the source for packaging, storage and opened-package instructions.
- Drying
- No drying value was confirmed by extraction; review the source.
- Equipment setup
- No equipment setting was confirmed by extraction; review the source.
- Applications
- Candidate application areas in the source: automotive. Verify the source, exact use and applicable approvals.
Source: the matched material PDF; page numbers refer to the original PDF.
- Application areas：page 2