聚醚酰亚胺
ULTEM™ Resin PW2100
Manufacturer：沙特基础工业公司
ULTEM PW2100树脂是一种无定形、不透明的聚醚酰亚胺（PEI）塑料，具有玻璃化转变温度（Tg）为217°C。
Recorded properties
Record date：2026-11-08
| Property | Value | Unit |
|---|---|---|
| Density | 1.34 | g/cm³ |
| Melt flow rate | 9.0 | g/10min |
| Tensile strength | 115.0 | MPa |
| Tensile modulus | 4500.0 | MPa |
| Elongation at break | 4.0 | % |
| Flexural modulus | 4500.0 | MPa |
| Notched impact strength | 30.0 | kJ/m² |
| Vicat softening point | 223.0 | °C |
| Flame rating | V-0 class | — |
Test standard, specimen condition and source rights are not fully recorded. Values are for preliminary screening only; verify with the manufacturer before design or purchasing decisions.
Grade handling information to verify
Verified grade-specific storage, drying, equipment settings and application details are not available in this record. Request the latest processing guide and safety data sheet for this exact grade from the manufacturer before establishing production settings.
- Storage
- Confirm packaging, temperature and humidity, shelf life, and handling after opening.
- Drying
- Confirm whether drying is required, plus temperature, time, dew point and target moisture.
- Equipment setup
- Confirm barrel and mold temperatures, injection conditions, residence time, purging and safe shutdown.
- Applications
- Confirm the manufacturer’s intended processes, application limits and relevant approvals for this grade.