玻璃纤维增强型无定形热塑性聚酰亚胺树脂
EXTEM™ Resin XH2315
Manufacturer：沙特基础工业公司
优异的机械、电气和尺寸性能，非常好的化学性能，固有阻燃性，符合RoHS标准
Recorded properties
Record date：2026-11-08
| Property | Value | Unit |
|---|---|---|
| Density | 1.52 | g/cm³ |
| Melt flow rate | 4.0 | g/10min |
| Tensile strength | 147.0 | MPa |
| Tensile modulus | 10500.0 | MPa |
| Elongation at break | 2.0 | % |
| Flexural modulus | 9000.0 | MPa |
| HDT 1.8MPa | 257.0 | °C |
| HDT 0.45MPa | 254.0 | °C |
| Vicat softening point | 267.0 | °C |
| Flame rating | UL94 V0 at 0.75 mm, V0,5VA at 1.0 mm and 1.5-1.65 mm | — |
Test standard, specimen condition and source rights are not fully recorded. Values are for preliminary screening only; verify with the manufacturer before design or purchasing decisions.
Grade handling information to verify
The information below was automatically extracted from a material PDF and has not been individually reviewed. It is for preliminary reference only. Verify the exact grade’s manufacturer processing instructions, safety data sheet and equipment procedures before production; do not use candidate values directly as machine settings.
Matched by original PDF filename
- Storage
- Review the source for packaging, storage and opened-package instructions.
- Drying
- Candidate injection-molding recommendations: temperature 175 °C; time 4 - 6 h; processing moisture ≤0.02 %. Verify the source, grade and conditions.
- Equipment setup
- Candidate injection-molding recommendations: melt temperature 380 - 405 °C; mold temperature 160 - 200 °C. Verify the source, grade and conditions.
- Applications
- Candidate application areas in the source: electrical and electronics. Verify the source, exact use and applicable approvals.
Source: the matched material PDF; page numbers refer to the original PDF.
- Drying temperature：page 1
- Drying time：page 2
- Processing moisture：page 2
- Melt temperature：page 2
- Mold temperature：page 2
- Application areas：page 2