Polyphenylene Ether (PPE) + High Impact Polystyrene (HIPS)
PX5373
Manufacturer：诺瑞尔
高耐热性，良好的介电强度，尺寸稳定性，水解稳定性，非常低的吸湿率
Recorded properties
Record date：2026-11-08
| Property | Value | Unit |
|---|---|---|
| Density | 1.25 | g/cm³ |
| Melt flow rate | 12.0 | g/10min |
| Tensile strength | 80.0 | MPa |
| Tensile modulus | 5500.0 | MPa |
| Elongation at break | 2.0 | % |
| Flexural modulus | 4500.0 | MPa |
| Notched impact strength | 30.0 | kJ/m² |
| Vicat softening point | 150.0 | °C |
| Flame rating | UL94 5VA at 2mm, V1 at 1.5mm | — |
Test standard, specimen condition and source rights are not fully recorded. Values are for preliminary screening only; verify with the manufacturer before design or purchasing decisions.
Grade handling information to verify
The information below was automatically extracted from a material PDF and has not been individually reviewed. It is for preliminary reference only. Verify the exact grade’s manufacturer processing instructions, safety data sheet and equipment procedures before production; do not use candidate values directly as machine settings.
Matched by original PDF filename
- Storage
- Review the source for packaging, storage and opened-package instructions.
- Drying
- Candidate injection-molding recommendations: temperature 100 - 120 °C; time 2 - 3 h. Verify the source, grade and conditions.
- Equipment setup
- Candidate injection-molding recommendations: melt temperature 280 - 300 °C; mold temperature 80 - 120 °C. Verify the source, grade and conditions.
- Applications
- Candidate application areas in the source: automotive. Verify the source, exact use and applicable approvals.
Source: the matched material PDF; page numbers refer to the original PDF.
- Drying temperature：page 2
- Drying time：page 2
- Melt temperature：page 2
- Mold temperature：page 2
- Application areas：page 2