Glass Reinforced Polyphenylene Ether (PPE) + High Impact Polystyrene (HIPS)
GFN1720
Manufacturer：诺瑞尔
良好的耐热性、强度和电气性能平衡
Recorded properties
Record date：2026-11-08
| Property | Value | Unit |
|---|---|---|
| Density | 1.24 | g/cm³ |
| Melt flow rate | 4.5 | g/10min |
| Tensile strength | 90.0 | MPa |
| Tensile modulus | 6000.0 | MPa |
| Elongation at break | 2.0 | % |
| Flexural modulus | 4500.0 | MPa |
| Notched impact strength | 25.0 | kJ/m² |
| HDT 1.8MPa | 171.0 | °C |
| Vicat softening point | 180.0 | °C |
| Flame rating | HB class | — |
Test standard, specimen condition and source rights are not fully recorded. Values are for preliminary screening only; verify with the manufacturer before design or purchasing decisions.
Grade handling information to verify
The information below was automatically extracted from a material PDF and has not been individually reviewed. It is for preliminary reference only. Verify the exact grade’s manufacturer processing instructions, safety data sheet and equipment procedures before production; do not use candidate values directly as machine settings.
Matched by original PDF filename
- Storage
- Review the source for packaging, storage and opened-package instructions.
- Drying
- Candidate injection-molding recommendations: temperature 110 - 120 °C; time 2 - 4 h. Verify the source, grade and conditions.
- Equipment setup
- Candidate injection-molding recommendations: melt temperature 290 - 330 °C; mold temperature 80 - 120 °C. Verify the source, grade and conditions.
- Applications
- Review the source and applicable approvals.
Source: the matched material PDF; page numbers refer to the original PDF.
- Drying temperature：page 2
- Drying time：page 2
- Melt temperature：page 2
- Mold temperature：page 2