玻璃纤维增强型聚苯醚/高冲击聚苯乙烯共混物
GFN3 - Europe
Manufacturer：诺瑞尔
低吸水率，高强度，水解稳定性，低翘曲，低密度，尺寸稳定性
Recorded properties
Record date：2026-11-08
| Property | Value | Unit |
|---|---|---|
| Density | 1.3 | g/cm³ |
| Melt flow rate | 7.0 | g/10min |
| Tensile strength | 100.0 | MPa |
| Tensile modulus | 8000.0 | MPa |
| Elongation at break | 1.5 | % |
| Flexural modulus | 6000.0 | MPa |
| Notched impact strength | 25.0 | kJ/m² |
| Vicat softening point | 155.0 | °C |
| Flame rating | UL746C outdoor suitability rating of F2 | — |
Test standard, specimen condition and source rights are not fully recorded. Values are for preliminary screening only; verify with the manufacturer before design or purchasing decisions.
Grade handling information to verify
The information below was automatically extracted from a material PDF and has not been individually reviewed. It is for preliminary reference only. Verify the exact grade’s manufacturer processing instructions, safety data sheet and equipment procedures before production; do not use candidate values directly as machine settings.
Matched by original PDF filename
- Storage
- Review the source for packaging, storage and opened-package instructions.
- Drying
- Candidate injection-molding recommendations: temperature 100 - 120 °C; time 2 - 4 h; processing moisture ≤0.02 %. Verify the source, grade and conditions.
- Equipment setup
- Candidate injection-molding recommendations: melt temperature 280 - 300 °C; mold temperature 80 - 120 °C. Verify the source, grade and conditions.
- Applications
- Candidate application areas in the source: automotive. Verify the source, exact use and applicable approvals.
Source: the matched material PDF; page numbers refer to the original PDF.
- Drying temperature：page 1
- Drying time：page 1
- Processing moisture：page 1
- Melt temperature：page 1
- Mold temperature：page 1
- Application areas：page 2