PPE+PS
N850
Manufacturer：NORYL™
高冲击强度，尺寸稳定性，水解稳定性，非常低的吸水率
Recorded properties
Record date：2026-11-08
| Property | Value | Unit |
|---|---|---|
| Density | 1.13 | g/cm³ |
| Melt flow rate | 18.0 | g/10min |
| Tensile strength | 66.0 | MPa |
| Tensile modulus | 2950.0 | MPa |
| Elongation at break | 3.2 | % |
| Flexural modulus | 2600.0 | MPa |
| HDT 1.8MPa | 82.0 | °C |
| HDT 0.45MPa | 95.0 | °C |
| Vicat softening point | 108.0 | °C |
| Flame rating | 5VA at 3mm and V0 at 1.5mm | — |
Test standard, specimen condition and source rights are not fully recorded. Values are for preliminary screening only; verify with the manufacturer before design or purchasing decisions.
Grade handling information to verify
The information below was automatically extracted from a material PDF and has not been individually reviewed. It is for preliminary reference only. Verify the exact grade’s manufacturer processing instructions, safety data sheet and equipment procedures before production; do not use candidate values directly as machine settings.
Matched by original PDF filename
- Storage
- Review the source for packaging, storage and opened-package instructions.
- Drying
- Candidate injection-molding recommendations: temperature 75 - 80 °C; time 3 - 4 h; processing moisture ≤0.02 %. Verify the source, grade and conditions.
- Equipment setup
- Candidate injection-molding recommendations: melt temperature 250 - 275 °C; mold temperature 55 - 75 °C. Verify the source, grade and conditions.
- Applications
- Review the source and applicable approvals.
Source: the matched material PDF; page numbers refer to the original PDF.
- Drying temperature：page 1
- Drying time：page 1
- Processing moisture：page 1
- Melt temperature：page 1
- Mold temperature：page 1