Polymer
PPX-GP1
Manufacturer：Polymer Resources, Ltd.
注塑成型
Recorded properties
Record date：2026-11-08
| Property | Value | Unit |
|---|---|---|
| Density | 1.06 | g/cm³ |
| Melt flow rate | 6.5 | g/10min |
| Tensile strength | 55.2 | MPa |
| Elongation at break | 30.0 | % |
| Flexural strength | 89.6 | MPa |
| Flexural modulus | 2413.0 | MPa |
| Notched impact strength | 14.7 | kJ/m² |
| HDT 1.8MPa | 129.0 | °C |
| HDT 0.45MPa | 121.0 | °C |
| Vicat softening point | 146.0 | °C |
| Flame rating | HB | — |
Test standard, specimen condition and source rights are not fully recorded. Values are for preliminary screening only; verify with the manufacturer before design or purchasing decisions.
Grade handling information to verify
The information below was automatically extracted from a material PDF and has not been individually reviewed. It is for preliminary reference only. Verify the exact grade’s manufacturer processing instructions, safety data sheet and equipment procedures before production; do not use candidate values directly as machine settings.
Matched by original PDF filename
- Storage
- Review the source for packaging, storage and opened-package instructions.
- Drying
- Candidate injection-molding recommendations: temperature 104 - 110 °C; time 3 - 4 h. Verify the source, grade and conditions.
- Equipment setup
- Candidate injection-molding recommendations: melt temperature 288 - 316 °C; mold temperature 71.1 - 93.3 °C. Verify the source, grade and conditions.
- Applications
- Review the source and applicable approvals.
Source: the matched material PDF; page numbers refer to the original PDF.
- Drying temperature：page 1
- Drying time：page 1
- Melt temperature：page 1
- Mold temperature：page 1