高冲击聚苯乙烯
PS ESCRimo
Manufacturer：斯泰诺路顿
高冲击或冲击改性
Recorded properties
Record date：2026-11-08
| Property | Value | Unit |
|---|---|---|
| Density | 1.04 | g/cm³ |
| Melt flow rate | 3.4 | g/10min |
| Tensile strength | 22.0 | MPa |
| Tensile modulus | 1550.0 | MPa |
| Elongation at break | 50.0 | % |
| Notched impact strength | 15.0 | kJ/m² |
| Vicat softening point | 89.0 | °C |
| Flame rating | HB class | — |
Test standard, specimen condition and source rights are not fully recorded. Values are for preliminary screening only; verify with the manufacturer before design or purchasing decisions.
Grade handling information to verify
The information below was automatically extracted from a material PDF and has not been individually reviewed. It is for preliminary reference only. Verify the exact grade’s manufacturer processing instructions, safety data sheet and equipment procedures before production; do not use candidate values directly as machine settings.
Matched by original PDF filename
- Storage
- Review the source for packaging, storage and opened-package instructions.
- Drying
- No drying value was confirmed by extraction; review the source.
- Equipment setup
- Candidate injection-molding recommendations: melt temperature 180 - 260 °C; mold temperature 10 - 60 °C. Verify the source, grade and conditions.
- Applications
- Review the source and applicable approvals.
Source: the matched material PDF; page numbers refer to the original PDF.
- Melt temperature：page 1
- Mold temperature：page 1