玻璃纤维增强聚苯硫醚
PSU-GF10
Manufacturer：西恩斯克
耐蠕变，耐化学，耐酸，耐碱，一般化学稳定性，水解稳定性
Recorded properties
Record date：2026-11-08
| Property | Value | Unit |
|---|---|---|
| Density | 1.33 | g/cm³ |
| Melt flow rate | 6.5 | g/10min |
| Tensile strength | 77.9 | MPa |
| Tensile modulus | 3720.0 | MPa |
| Elongation at break | 4.0 | % |
| Flexural strength | 128.0 | MPa |
| Flexural modulus | 3790.0 | MPa |
| Notched impact strength | 48.0 | kJ/m² |
| HDT 1.8MPa | 179.0 | °C |
| Flame rating | HB | — |
Test standard, specimen condition and source rights are not fully recorded. Values are for preliminary screening only; verify with the manufacturer before design or purchasing decisions.
Grade handling information to verify
The information below was automatically extracted from a material PDF and has not been individually reviewed. It is for preliminary reference only. Verify the exact grade’s manufacturer processing instructions, safety data sheet and equipment procedures before production; do not use candidate values directly as machine settings.
Matched by original PDF filename
- Storage
- Review the source for packaging, storage and opened-package instructions.
- Drying
- Candidate injection-molding recommendations: temperature 149 - 163 °C; time 3 - 4 h. Verify the source, grade and conditions.
- Equipment setup
- Candidate injection-molding recommendations: melt temperature 343 - 399 °C; mold temperature 121 - 163 °C. Verify the source, grade and conditions.
- Applications
- Review the source and applicable approvals.
Source: the matched material PDF; page numbers refer to the original PDF.
- Drying temperature：page 1
- Drying time：page 1
- Melt temperature：page 1
- Mold temperature：page 1