ABS
ABS_ColorFast® GPA100
Manufacturer：美国化工公司
高冲击或冲击改性
Recorded properties
Record date：2026-11-07
| Property | Value | Unit |
|---|---|---|
| Density | 1.05 | g/cm³ |
| Melt flow rate | 6.0 | g/10min |
| Tensile strength | 44.8 | MPa |
| Elongation at break | 26.0 | % |
| Flexural strength | 68.9 | MPa |
| Flexural modulus | 2137.0 | MPa |
| Notched impact strength | 320.0 | kJ/m² |
| HDT 1.8MPa | 82.2 | °C |
| Flame rating | HB | — |
Test standard, specimen condition and source rights are not fully recorded. Values are for preliminary screening only; verify with the manufacturer before design or purchasing decisions.
Grade handling information to verify
The information below was automatically extracted from a material PDF and has not been individually reviewed. It is for preliminary reference only. Verify the exact grade’s manufacturer processing instructions, safety data sheet and equipment procedures before production; do not use candidate values directly as machine settings.
Matched by original PDF filename
- Storage
- Review the source for packaging, storage and opened-package instructions.
- Drying
- Candidate injection-molding recommendations: temperature 82.2 - 93.3 °C; time 2 - 4 h. Verify the source, grade and conditions.
- Equipment setup
- Candidate injection-molding recommendations: melt temperature 218 - 260 °C; mold temperature 48.9 - 71.1 °C. Verify the source, grade and conditions.
- Applications
- Review the source and applicable approvals.
Source: the matched material PDF; page numbers refer to the original PDF.
- Drying temperature：page 1
- Drying time：page 1
- Melt temperature：page 1
- Mold temperature：page 1