ASA
ASA LI913
Manufacturer：LG化学
高冲击或冲击改性，紫外线稳定或耐候性好
Recorded properties
Record date：2026-11-07
| Property | Value | Unit |
|---|---|---|
| Density | 1.07 | g/cm³ |
| Melt flow rate | 6.0 | g/10min |
| Tensile strength | 40.2 | MPa |
| Tensile modulus | 1727.0 | MPa |
| Elongation at break | 5.0 | % |
| Flexural strength | 64.7 | MPa |
| Flexural modulus | 1913.0 | MPa |
| Notched impact strength | 441.0 | kJ/m² |
| HDT 1.8MPa | 96.0 | °C |
| HDT 0.45MPa | 86.0 | °C |
| Vicat softening point | 94.0 | °C |
| Flame rating | HB | — |
Test standard, specimen condition and source rights are not fully recorded. Values are for preliminary screening only; verify with the manufacturer before design or purchasing decisions.
Grade handling information to verify
The information below was automatically extracted from a material PDF and has not been individually reviewed. It is for preliminary reference only. Verify the exact grade’s manufacturer processing instructions, safety data sheet and equipment procedures before production; do not use candidate values directly as machine settings.
Matched by original PDF filename
- Storage
- Review the source for packaging, storage and opened-package instructions.
- Drying
- No drying value was confirmed by extraction; review the source.
- Equipment setup
- No equipment setting was confirmed by extraction; review the source.
- Applications
- Candidate application areas in the source: electrical and electronics. Verify the source, exact use and applicable approvals.
Source: the matched material PDF; page numbers refer to the original PDF.
- Application areas：page 1