Extrusion Copolymer
Halar® 930LC
Manufacturer：森斯克欧
缺口冲击强度1/8英寸N J/m，低温缺口冲击强度210 J/m，模具收缩率，MD 0.025 mm/mm，拉伸模量1660 MPa，屈服强度30 MPa，断裂强度54 MPa，屈服伸长率5 %，断裂伸长率250 %，弯曲模量1690 MPa，弯曲强度47 MPa，洛氏硬度R 90，肖氏硬度D 75，线性膨胀系数，MD 100 E-6/K，66 psi时的DTUL 90 °C，264 psi时的DTUL 65 °C，熔点242 °C，限制氧指数52 %，短时击穿强度14 kV/mm，1 MHz时的介电常数2.57，
Recorded properties
Record date：2026-11-07
| Property | Value | Unit |
|---|---|---|
| Density | 1.68 | g/cm³ |
| Melt flow rate | 4.5 | g/10min |
| Tensile strength | 54.0 | MPa |
| Tensile modulus | 1660.0 | MPa |
| Elongation at break | 250.0 | % |
| Flexural strength | 47.0 | MPa |
| Flexural modulus | 1690.0 | MPa |
| Notched impact strength | 210.0 | kJ/m² |
| HDT 1.8MPa | 90.0 | °C |
| HDT 0.45MPa | 65.0 | °C |
| Flame rating | V-0 | — |
Test standard, specimen condition and source rights are not fully recorded. Values are for preliminary screening only; verify with the manufacturer before design or purchasing decisions.
Grade handling information to verify
Verified grade-specific storage, drying, equipment settings and application details are not available in this record. Request the latest processing guide and safety data sheet for this exact grade from the manufacturer before establishing production settings.
- Storage
- Confirm packaging, temperature and humidity, shelf life, and handling after opening.
- Drying
- Confirm whether drying is required, plus temperature, time, dew point and target moisture.
- Equipment setup
- Confirm barrel and mold temperatures, injection conditions, residence time, purging and safe shutdown.
- Applications
- Confirm the manufacturer’s intended processes, application limits and relevant approvals for this grade.