SURLYN™ 8920
Manufacturer：陶氏化学公司
注塑成型，片材挤出，其他挤出，吹塑成型
Recorded properties
Record date：2026-11-07
| Property | Value | Unit |
|---|---|---|
| Density | 0.95 | g/cm³ |
| Melt flow rate | 0.9 | g/10min |
| Tensile strength | 15.2 | MPa |
| Elongation at break | 350.0 | % |
| Flexural modulus | 380.0 | MPa |
| Notched impact strength | 635.0 | kJ/m² |
| Vicat softening point | 57.8 | °C |
Test standard, specimen condition and source rights are not fully recorded. Values are for preliminary screening only; verify with the manufacturer before design or purchasing decisions.
Grade handling information to verify
The information below was automatically extracted from a material PDF and has not been individually reviewed. It is for preliminary reference only. Verify the exact grade’s manufacturer processing instructions, safety data sheet and equipment procedures before production; do not use candidate values directly as machine settings.
Matched by original PDF filename
- Storage
- Review the source for packaging, storage and opened-package instructions.
- Drying
- No drying value was confirmed by extraction; review the source.
- Equipment setup
- Candidate injection-molding recommendations: melt temperature 185 - 285 °C. Verify the source, grade and conditions.
- Applications
- Review the source and applicable approvals.
Source: the matched material PDF; page numbers refer to the original PDF.
- Melt temperature：page 1