PA66-GF13
PA66-GF13_Vydyne® R513H NT
Manufacturer：Ascend
高冲击或冲击改性，耐热稳定
Recorded properties
Record date：2026-11-07
| Property | Value | Unit |
|---|---|---|
| Density | 1.23 | g/cm³ |
| Tensile strength | 115.0 | MPa |
| Tensile modulus | 6200.0 | MPa |
| Elongation at break | 3.0 | % |
| Flexural strength | 165.0 | MPa |
| Flexural modulus | 5200.0 | MPa |
| Notched impact strength | 6.0 | kJ/m² |
| HDT 1.8MPa | 240.0 | °C |
| HDT 0.45MPa | 258.0 | °C |
| Flame rating | {'HB': 'HB', 'GWFI': 675, 'GWIT': 700} | — |
Test standard, specimen condition and source rights are not fully recorded. Values are for preliminary screening only; verify with the manufacturer before design or purchasing decisions.
Grade handling information to verify
The information below was automatically extracted from a material PDF and has not been individually reviewed. It is for preliminary reference only. Verify the exact grade’s manufacturer processing instructions, safety data sheet and equipment procedures before production; do not use candidate values directly as machine settings.
Matched by original PDF filename
- Storage
- Review the source for packaging, storage and opened-package instructions.
- Drying
- Candidate injection-molding recommendations: temperature 80 °C; time 4 h. Verify the source, grade and conditions.
- Equipment setup
- Candidate injection-molding recommendations: melt temperature 285 - 305 °C; mold temperature 65 - 95 °C. Verify the source, grade and conditions.
- Applications
- Candidate application areas in the source: automotive. Verify the source, exact use and applicable approvals.
Source: the matched material PDF; page numbers refer to the original PDF.