PA66-GF
PA66-GF LATAMID 66 H2 G35-V0KB3
Manufacturer：LATI工业热塑性公司
热稳定或耐热
Recorded properties
Record date：2026-11-07
| Property | Value | Unit |
|---|---|---|
| Density | 1.45 | g/cm³ |
| Tensile strength | 145.0 | MPa |
| Tensile modulus | 9800.0 | MPa |
| Elongation at break | 2.2 | % |
| Notched impact strength | 10.0 | kJ/m² |
| HDT 1.8MPa | 245.0 | °C |
| HDT 0.45MPa | 260.0 | °C |
| Vicat softening point | 250.0 | °C |
| Flame rating | {'glow_wire_flammability_index_1_mm': '960', 'glow_wire_flammability_index_2_mm': '960', 'glow_wire_ignition_temperature_1_mm': '725', 'glow_wire_ignition_temperature_2_mm': '775', 'ul_94_flame_rating': 'V-0', 'thickness_tested': '0.75 mm'} | — |
Test standard, specimen condition and source rights are not fully recorded. Values are for preliminary screening only; verify with the manufacturer before design or purchasing decisions.
Grade handling information to verify
The information below was automatically extracted from a material PDF and has not been individually reviewed. It is for preliminary reference only. Verify the exact grade’s manufacturer processing instructions, safety data sheet and equipment procedures before production; do not use candidate values directly as machine settings.
Matched by original PDF filename
- Storage
- Review the source for packaging, storage and opened-package instructions.
- Drying
- Candidate injection-molding recommendations: temperature 90 - 100 °C; time 3 h. Verify the source, grade and conditions.
- Equipment setup
- Candidate injection-molding recommendations: melt temperature 270 - 290 °C; mold temperature 70 - 100 °C. Verify the source, grade and conditions.
- Applications
- Review the source and applicable approvals.
Source: the matched material PDF; page numbers refer to the original PDF.
- Drying temperature：page 1
- Drying time：page 1
- Melt temperature：page 1
- Mold temperature：page 1