PBT
WF006NAiQ
Manufacturer：LNP™ ELCRIN™
iQ PBT基复合材料，含有30%玻璃，适用于NMT应用。该材料的附加功能包括：>25% PCR，高金属结合强度和良好的化学抗性。
Recorded properties
Record date：2026-11-07
| Property | Value | Unit |
|---|---|---|
| Density | 1.48 | g/cm³ |
| Melt flow rate | 24.0 | g/10min |
| Tensile strength | 111.0 | MPa |
| Tensile modulus | 8700.0 | MPa |
| Elongation at break | 2.6 | % |
| Flexural strength | 173.0 | MPa |
| Flexural modulus | 7400.0 | MPa |
| Notched impact strength | 14.5 | kJ/m² |
| HDT 1.8MPa | 206.0 | °C |
| HDT 0.45MPa | 172.0 | °C |
Test standard, specimen condition and source rights are not fully recorded. Values are for preliminary screening only; verify with the manufacturer before design or purchasing decisions.
Grade handling information to verify
Verified grade-specific storage, drying, equipment settings and application details are not available in this record. Request the latest processing guide and safety data sheet for this exact grade from the manufacturer before establishing production settings.
- Storage
- Confirm packaging, temperature and humidity, shelf life, and handling after opening.
- Drying
- Confirm whether drying is required, plus temperature, time, dew point and target moisture.
- Equipment setup
- Confirm barrel and mold temperatures, injection conditions, residence time, purging and safe shutdown.
- Applications
- Confirm the manufacturer’s intended processes, application limits and relevant approvals for this grade.
You may consult the family overview; it does not provide verified settings for this grade: Material-family guide