Polycarbonate/Acrylonitrile Butadiene Styrene (PC/ABS) blend containing 20% carbon fiber
LEXAN™ FR Resin JK2500
Manufacturer：沙特基础工业公司
导电性，电磁干扰/射频干扰屏蔽效果为1.5mm时的21dB，非溴化，非氯化阻燃剂
Recorded properties
Record date：2026-11-07
| Property | Value | Unit |
|---|---|---|
| Density | 1.31 | g/cm³ |
| Melt flow rate | 25.0 | g/10min |
| Tensile strength | 63.0 | MPa |
| Tensile modulus | 11100.0 | MPa |
| Elongation at break | 2.3 | % |
| Flexural modulus | 10100.0 | MPa |
| Notched impact strength | 5.0 | kJ/m² |
| HDT 1.8MPa | 98.0 | °C |
| Vicat softening point | 100.0 | °C |
| Flame rating | V-0 class | — |
Test standard, specimen condition and source rights are not fully recorded. Values are for preliminary screening only; verify with the manufacturer before design or purchasing decisions.
Grade handling information to verify
The information below was automatically extracted from a material PDF and has not been individually reviewed. It is for preliminary reference only. Verify the exact grade’s manufacturer processing instructions, safety data sheet and equipment procedures before production; do not use candidate values directly as machine settings.
Matched by original PDF filename
- Storage
- Review the source for packaging, storage and opened-package instructions.
- Drying
- Candidate injection-molding recommendations: temperature 80 - 90 °C; time 3 - 4 h. Verify the source, grade and conditions.
- Equipment setup
- Candidate injection-molding recommendations: melt temperature 270 - 310 °C; mold temperature 50 - 95 °C. Verify the source, grade and conditions.
- Applications
- Review the source and applicable approvals.
Source: the matched material PDF; page numbers refer to the original PDF.
- Drying temperature：page 1
- Drying time：page 1
- Melt temperature：page 1
- Mold temperature：page 1