PC+ABS
PC+ABS_LOXILLOY PCABS 1120-12 05012
Manufacturer：洛希姆工业有限公司
高冲击或冲击改性，耐热或对热稳定
Recorded properties
Record date：2026-11-07
| Property | Value | Unit |
|---|---|---|
| Density | 1.13 | g/cm³ |
| Melt flow rate | 12.0 | g/10min |
| Tensile strength | 52.0 | MPa |
| Elongation at break | 50.0 | % |
| Flexural strength | 85.0 | MPa |
| Flexural modulus | 2550.0 | MPa |
| Notched impact strength | 41.0 | kJ/m² |
| HDT 1.8MPa | 100.0 | °C |
| HDT 0.45MPa | 122.0 | °C |
| Vicat softening point | 120.0 | °C |
Test standard, specimen condition and source rights are not fully recorded. Values are for preliminary screening only; verify with the manufacturer before design or purchasing decisions.
Grade handling information to verify
The information below was automatically extracted from a material PDF and has not been individually reviewed. It is for preliminary reference only. Verify the exact grade’s manufacturer processing instructions, safety data sheet and equipment procedures before production; do not use candidate values directly as machine settings.
Matched by original PDF filename
- Storage
- Review the source for packaging, storage and opened-package instructions.
- Drying
- No drying value was confirmed by extraction; review the source.
- Equipment setup
- No equipment setting was confirmed by extraction; review the source.
- Applications
- Candidate application areas in the source: automotive. Verify the source, exact use and applicable approvals.
Source: the matched material PDF; page numbers refer to the original PDF.
- Application areas：page 1